ORIGINAL ARTICLE  
Year : 2022  |  Volume : 25  |  Issue : 4  |  Page : 426-430
Effect of triple antibiotic paste on the bond strength of epoxy and methacrylate resin-based sealers to root canal dentin


1 Departments of Endodontics and School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran
2 Department of Endodontics, Biomaterials Research Center, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran
3 Dental Student, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran

Click here for correspondence address and email

Date of Submission13-Mar-2022
Date of Decision02-May-2022
Date of Acceptance17-May-2022
Date of Web Publication02-Aug-2022
 

   Abstract 

Purpose: This study aimed to evaluate the effect of triple antibiotic paste (TAP) as an endodontic intracanal medicament on the bond strength of epoxy and methacrylate resin-based sealers to root canal dentin.
Materials and Methods: In this in vitro study, 80 single-rooted human mandibular premolars were prepared using ProTaper rotary system. The specimens were randomly divided into a control group (without intracanal dressing) and an experimental group receiving TAP (n = 40). The intracanal dressing was removed after 3 weeks. Then, samples of each group were randomly divided into four subgroups (n = 10) and obturated with gutta-percha and different resin-based sealers. G1: AH Plus, G2: Syntex, G3: EndoREZ, and G4: MetaSEAL. After 1 week, 16 slices of 1 ± 0.1 mm thickness were obtained from the midroots of teeth in each subgroup, and a push-out test was used to measure the bond strength. Slices were examined using a stereomicroscope at 30 × to determine the mode of failure. The data were analyzed using two-way analysis of variance, one-way analysis of variance, and Tukey post hoc tests (α = 0.05).
Results: Compared to control group, TAP significantly increased the bond strength of MetaSEAL and EndoREZ (P < 0.05). In the control group, epoxy resin-based sealers showed higher bond strength compared to methacrylate ones (P = 0.00). In TAP group, Syntex and EndoREZ showed significantly the greatest and the lowest bond strengths, respectively, (P < 0.05). The analysis of failure modes revealed a predominance of mixed failures in all groups except for Syntex group in which most failures were cohesive.
Conclusions: TAP significantly increased the bond strength of methacrylate resin-based sealers.

Keywords: AH plus; bond strength; EndoREZ; MetaSEAL; Syntex; triple antibiotic paste

How to cite this article:
Sobhnamayan F, Adl A, Sedigh-Shams M, Mirkhaghani H. Effect of triple antibiotic paste on the bond strength of epoxy and methacrylate resin-based sealers to root canal dentin. J Conserv Dent 2022;25:426-30

How to cite this URL:
Sobhnamayan F, Adl A, Sedigh-Shams M, Mirkhaghani H. Effect of triple antibiotic paste on the bond strength of epoxy and methacrylate resin-based sealers to root canal dentin. J Conserv Dent [serial online] 2022 [cited 2022 Aug 12];25:426-30. Available from: https://www.jcd.org.in/text.asp?2022/25/4/426/353135

   Introduction Top


Complete eradication of microorganisms and their byproducts from the root canal system is impossible even after chemomechanical preparation in any form.[1] Therefore, application of intracanal medicaments has been suggested for further reduction of bacterial load.[2],[3] Calcium hydroxide (CH) is the most commonly used intracanal medicament due to its antibacterial and anti-inflammatory effects, and ability to dissolve remnants of pulpal tissue.[4] However, some deficits such as inability in the elimination of Enterococcus Faecalis[5] and being potentially toxic due to its high pH makes investigators to search for new therapeutic agents to be used as alternative intracanal medicaments.[5] Due to polymicrobial nature of endodontic infections, a mixture of different antibiotics has also been proposed as potential intracanal medicaments.[6]

Triple antibiotic paste (TAP), consisting of metronidazole, ciprofloxacin, and minocycline, is used in endodontics not only in the regeneration and revascularization protocol of the pulp but also for the treatment of periapical lesions, external inflammatory root resorption, root fracture, and primary teeth.[7]

This endodontic medicament has been found to have excellent antimicrobial properties and to be biocompatible.[8],[9] Studies demonstrated that the use of TAP as an intracanal medicament increased the dentinal tubule disinfection[10] and penetration area of the medicament[11] compared with CH.

Despite of all favorable characteristic of TAP, similar to other intracanal medicaments, it cannot be completely cleaned from the root canal.[12],[13] Moreover, it has been showed that TAP changes the chemical structure of dentin.[14],[15] Therefore, in teeth treated with this medicament, the bonding of endodontic sealers to radicular dentin may be affected. Nevertheless, limited studies have been published concerning the impact of TAP on the bond strength of resin-based sealers to root dentin.

In one study conducted by Akcay et al. pretreatment with TAP enhanced the bond strength of AH Plus, an epoxy resin-based sealer, to the root canal dentin.[16] However, this study suffers from the fact that only one endodontic sealer was evaluated. Moreover, to the best of our knowledge, there are no data regarding the effect of pretreatment with TAP on the adherence of methacrylate resin-based sealers to the radicular dentin. Therefore, the aim of the present study was to evaluate and compare the effect of pretreatment with TAP on the bond strength of two epoxy (AH Plus and Syntex) and two methacrylate (EndoREZ and MetaSEAL) resin-based sealers.


   Materials and Methods Top


The study was approved by the Ethics Committee of the Shiraz University of Medical Sciences (REC.1396.S94). All methods were carried out in accordance with relevant guidelines and regulations.

Eighty human mandibular premolar teeth extracted for clinical reasons with the patients' informed consent were used in this study. A buccolingual radiograph was taken for each tooth to ensure the presence of a single canal. Exclusion criteria were open apices, resorptions, cracks, or previous root canal treatments.

The teeth were disinfected by immersion in 0.5% chloramines T solution for 48 h and then kept in distilled water until use.

Each tooth was decoronated to obtain a standardized root length of 15 mm. Working length was established by subtracting 1 mm from length of a size 10 K-file that its tip was visible at the apical foramen. Cleaning and shaping were done using ProTaper rotary files (Dentsply Maillefer) up to size F4 (#40/0.06). Irrigation with 2 mL of 2.5% sodium hypochlorite (Chloraxid, Cerkamed, Poland) was performed before using each file.

At the end of preparation, each canal was rinsed with 5 mL 17% EDTA and 5 mL 1% NaOCl each for 1 min, and dried. At this stage, the specimens were randomly allocated into a control group of no intracanal medicament (n = 40) and an experimental group receiving TAP as intracanal medicament (n = 40). TAP was prepared by taking equal amounts of powdered metronidazole (Metromax, Tehran Chemie, Tehran, Iran), ciprofloxacin (Ciproted, Tehran Darou Co., Tehran), and minocycline (Minocin, Watson Pharmaceuticals Inc., California, USA) and mixing them with sterilized distilled water in a powder/liquid ratio of 3:1.

Lentulo spirals number 40 were used to transferred the prepared paste into the root canals. Then, the coronal openings were temporarily sealed with a cotton pellet and temporary restorative material (Cavisol, Golchai Co., Iran), and the samples were kept in an incubator at 37°C in 100% humidity for 21 days.[17] At the end of incubation period, TAP was removed by needle irrigation of canals with 10 mL 17% EDTA, followed by 10 mL 2.5% NaOCl[12] and a final flush of 5-mL distilled water. In the next step, the samples of both control group and experimental group were divided into four subgroups based on the sealers used for obturation of the root canals. Two epoxy resin-based sealers: G1: AH Plus (Dentsply DeTrey, Konstanz, Germany) and G2: Syntex (Cerkamed, Stalowa Wola, Poland) and two methacrylate resin-based sealers: G3: EndoREZ (Ultradent, South Jordan, Utah, UAS) and G4: MetaSEAL (Parkell Inc, Edgewood, NY) were used.

Obturation in all groups was performed by a single-cone technique with use of F4 gutta-percha cones combined with one of tested sealers. The F4 gutta-percha cones (Dentsply Maillefer, Ballaigues, Switzerland) were coated with respected sealers and inserted into the root canal up to the working length. The excess gutta-percha and sealer in the coronal portion were removed, and in the methacrylate resin-based sealer groups (G3, G4), the coronal surface was light cured for 40 s.

After that, the coronal openings were sealed with a temporary filling material, and the specimens were stored for 1 week at 37°C and 100% humidity to allow the sealers to set. Each root was then sectioned perpendicular to its long axis using a low speed saw (Mecatom T180; Presi SA, Angonnes, France) under continuous water irrigation. Two slices (1 ± 0.1 mm thick) were obtained from the midroot of each tooth (n = 20). The slices were checked under a stereomicroscope, and finally, 16 discs with round lumen were chosen from each subgroup.

A digital camera attached to a stereomicroscopic (Bestscope-3060c, China) was used to capture images from coronal and apical aspects of each slice under 32 × magnification. Scope image software (Bestscope-3060c, China) was then used to measure the lumen diameters of both sides of the slices.

A universal testing machine (ZwickRoell, Z050; ZwickRoell, Ulm, Germany) was used for the push-out bond strength test, at a crosshead speed of 1 mm/min and with a 0.5-mm diameter cylindrical plunge. Loading was performed in an apical-coronal direction until the displacement of the filling material. The maximum load before failure was recorded in newton and divided by the adhesion area, resulting in a bond strength expression in mega Pascal (MPa).

The adhesion area of the root canal filling was calculated using the following formula:

π (R + r) [h2 + (Rr)2]0.5, where π is the constant 3.14, R is the radius of the coronal side, r is the radius of the apical side, and h represents the thickness of the root slice.[18]

After the test procedure, the specimens were observed under a stereomicroscope at 32× magnification to determine the mode of failure. Three types of failure were categorized: adhesive failure (at the sealer dentin interface), cohesive fracture (within the filing material or dentin), and mixed failure (a mixture of cohesive and adhesive failures).[19]

Statistical analysis

The data were analyzed using two-way analysis of variance. As there was a significant interaction effect between using TAP and the root canal sealers, one-way analysis of variance and post hoc Tukey's tests were used to detect the effect of the independent variables (using TAP and sealers) on the bond strength. All statistical analyses were done using SPSS (version 20, SPSS Inc., Chicago, IL, USA) at a significance level of 0.05.


   Results Top


A significant interaction effect was found between sealer types and using TAP (P < 0.05).

The mean and standard deviation of the push-out bond strength values (MPa) of the sealers to the radicular dentin are indicated in [Table 1].
Table 1: Mean±standard deviation of pus-out bond strength values

Click here to view


Compared to control group, TAP significantly increased the bond strength of methacrylate resin-based sealers (P = 0.0001 and P = 0.002 for MetaSEAL and EndoREZ, respectively). In epoxy resin-based sealers (AH Plus and Syntex), the increase in the bond strength was not significant (P > 0.05).

In the control group, the epoxy resin-based sealers showed significantly higher bond strength compared to the methacrylate resin-based sealers (P = 0.0001). In the TAP group, the greatest and the lowest bond strengths were belonged to Syntex and EndoREZ, respectively, which were significantly different from other sealers (P <.05).

The analysis of failure modes showed a predominance of mixed failure in all groups with the exception of Syntex group in which most failures were cohesive.


   Discussion Top


Adhesion of endodontic sealers to intraradicular dentin is an important property for two main reasons. In a static situation, it prevents the passage of fluids between the filing material and the radicular dentin.[20] In a dynamic situation, it minimizes the risk of dislodgment of root canal filing material during the restorative procedures or masticatory function.[21],[22] Actually, it has been reported that sealing ability and bond strength of endodontic sealers may strongly correlate with each other.[23]

According to the result of the present study, TAP increased the bond strength of all tested resin-based sealers. However, the increase was statistically significant only for the methacrylate resin-based sealers.

Our findings are partly in accordance with those of Akcay et al.[16] who evaluated the effects of CH, TAP, and double antibiotic paste (DAP) on the bond strength of an epoxy resin-based sealer (AH Plus) to the radicular dentin. They reported higher bond strength in the TAP group, whereas DAP and CH did not show any promising effect. The authors[16] attributed their finding to the binding of residual minocycline to the calcium ions of dentinal walls through a chelation reaction. Although this theory may explain the incomplete removal of TAP from the root canals, we believe it does not clarify how the tested sealer bonded to the residual of TAP and in this way to the dentinal wall.

In our opinion, the increase of the bond strength of resin-based sealers to dentin after application of TAP could be attributed to the strong demineralizing and erosive effect of this medicament on the radicular dentin due to its low pH value.[14],[24],[25] This erosive effect increases the adhesion surfaces, which in turn may improve the adhesion of sealers to dentin. Further studies are recommended to assess the changes in the topography of dentin after application of TAP. In addition, a decline in the phosphate/amide I ratio has been reported after treatment of dentin with TAP.[26] This chemical change may also have a promising effect on the bond strength of resin-based sealers to dentin. More investigations are needed to verify these theories.

In another study, Shakouie et al.[27] concluded that the effect of TAP on the bond strength of endodontic sealers was not negative. However, as their study had no control (no medicament) group, its comparison with the current study seems not to be logical.

On the other hand, in the study of Arslan et al.,[28] TAP decreased the bond strength of a self-adhesive resin cement (RelyX U200; 3M ESPE, Seefeld, Germany) to the root dentin. As normally the acid groups of this cement chemically interact with calcium ions of hydroxyapatite crystals, the authors discussed that the bonding strength would be adversely affected because the calcium ions had been previously chelated by minocycline. The authors also mentioned that the incomplete removal of TAP from the canal walls could be another possible reason for decrease of bond strength. The discrepancy between the results of Arslan et al. study[28] and the present study could be attributed to the different types of material used (resin cement versus resin sealers) and also different protocols used for removal of TAP.

The result of the present study showed that in the control group, both epoxy resin-based sealers presented significantly higher bond strength than both of methacrylate resin-based sealers. This finding is in agreement with the result of previous studies comparing the bond strength of these two subgroups of resin-based sealers.[29],[30],[31]

The stronger adhesion of epoxy resin-based sealers has been attributed to the lower volumetric polymerization shrinkage and higher penetration to the dentinal tubules.[32],[33],[34]

In the current study, Syntex showed the maximum bond strength both in control and in TAP groups. Its difference was even significant with AH, another epoxy based sealer, in TAP group. Syntex is a new epoxy resin-based sealer that according to its manufacturer has minimal shrinkage upon setting, particles of the smallest possible size, and excellent penetration properties. These features can explain the good adhesion of this sealer found in the current study. In addition, evaluation of the root dicks after the push-out test demonstrated a predominance of cohesive failure for Syntex but mixed failure for other groups, which confirms the better adhesive performance of this new epoxy resin-based sealer.


   Conclusions Top


Under the limitation of this in vitro study, it can be concluded that TAP improved the bond strength of the methacrylate resin-based sealers.

Data availability

The data that support the findings of this study are available from the corresponding author, upon reasonable request

Acknowledgements

The authors thank the Vic-Chancellery of Shiraz University of Medical Science for supporting this research. The authors also thank Dr.Vossoughi from the Center for Research Improvement of the School of Dentistry for the statistical analysis.

Financial support and sponsorship

Nil.

Conflicts of interest

There are no conflicts of interest.



 
   References Top

1.
Barbizam JV, Fariniuk LF, Marchesan MA, Pecora JD, Sousa-Neto MD. Effectiveness of manual and rotary instrumentation techniques for cleaning flattened root canals. J Endod 2002;28:365-6.  Back to cited text no. 1
    
2.
Estrela C, Holland R, Bernabé PF, de Souza V, Estrela CR. Antimicrobial potential of medicaments used in healing process in dogs' teeth with apical periodontitis. Braz Dent J 2004;15:181-5.  Back to cited text no. 2
    
3.
Athanassiadis B, Abbott PV, Walsh LJ. The use of calcium hydroxide, antibiotics and biocides as antimicrobial medicaments in endodontics. Aust Dent J 2007;52:S64-82.  Back to cited text no. 3
    
4.
Bystrom A, Claesson R, Sundqvist G. The antibacterial effect of camphorated paramonochlorophenol, camphorated phenol and calcium hydroxide in the treatment of infected root canals. Endod Dent Traumatol 1985;1:170-5.  Back to cited text no. 4
    
5.
Siqueira JF Jr., Lopes HP. Mechanisms of antimicrobial activity of calcium hydroxide: A critical review. Int Endod J 1999;32:361-9.  Back to cited text no. 5
    
6.
Taneja S, Kumari M. Use of triple antibiotic paste in the treatment of large periradicular lesions. J Investig Clin Dent 2012;3:72-6.  Back to cited text no. 6
    
7.
Parhizkar A, Nojehdehian H, Asgary S. Triple antibiotic paste: Momentous roles and applications in endodontics: A review. Restor Dent Endod 2018;43:e28.  Back to cited text no. 7
    
8.
Thibodeau B, Teixeira F, Yamauchi M, Caplan DJ, Trope M. Pulp revascularization of immature dog teeth with apical periodontitis. J Endod 2007;33:680-9.  Back to cited text no. 8
    
9.
Gomes-Filho JE, Duarte PC, de Oliveira CB, Watanabe S, Lodi CS, Cintra LT, et al. Tissue reaction to a triantibiotic paste used for endodontic tissue self-regeneration of nonvital immature permanent teeth. J Endod 2012;38:91-4.  Back to cited text no. 9
    
10.
Adl A, Hamedi S, Sedigh Shams M, Motamedifar M, Sobhnamayan F. The ability of triple antibiotic paste and calcium hydroxide in disinfection of dentinal tubules. Iran Endod J 2014;9:123-6.  Back to cited text no. 10
    
11.
Deniz Sungur D, Aksel H, Purali N. Effect of a low surface tension vehicle on the dentinal tubule penetration of calcium hydroxide and triple antibiotic paste. J Endod 2017;43:452-5.  Back to cited text no. 11
    
12.
Arslan H, Capar ID, Saygili G, Uysal B, Gok T, Ertas H, et al. Efficacy of various irrigation protocols on the removal of triple antibiotic paste. Int Endod J 2014;47:594-9.  Back to cited text no. 12
    
13.
Rouhani A, Erfanzadeh M, Jafarzadeh H, Najafi E. Comparison of residual triple antibiotic paste, propolis and calcium hydroxide on root canal walls in natural open apex teeth: An in vitro study. Iran Endod J 2018;13:25-9.  Back to cited text no. 13
    
14.
Yassen GH, Chu TM, Eckert G, Platt JA. Effect of medicaments used in endodontic regeneration technique on the chemical structure of human immature radicular dentin: An in vitro study. J Endod 2013;39:269-73.  Back to cited text no. 14
    
15.
Verma P, Ansari A, Tikku AP, Chandra A, Yadav RK, Bharti R, et al. Effect of intracanal medicaments on radicular dentine: An attenuated total reflection-Fourier-transform infrared spectroscopy analysis. Asian J Oral Health Allied Sci 2020;10:3.  Back to cited text no. 15
    
16.
Akcay M, Arslan H, Topcuoglu HS, Tuncay O. Effect of calcium hydroxide and double and triple antibiotic pastes on the bond strength of epoxy resin-based sealer to root canal dentin. J Endod 2014;40:1663-7.  Back to cited text no. 16
    
17.
Carmen L, Asunción M, Beatriz S, Rosa YV. Revascularization in immature permanent teeth with necrotic pulp and apical pathology: Case series. Case Rep Dent 2017;2017:3540159.  Back to cited text no. 17
    
18.
Prado M, Simão RA, Gomes BP. Effect of different irrigation protocols on resin sealer bond strength to dentin. J Endod 2013;39:689-92.  Back to cited text no. 18
    
19.
Nagas E, Uyanik MO, Eymirli A, Cehreli ZC, Vallittu PK, Lassila LV, et al. Dentin moisture conditions affect the adhesion of root canal sealers. J Endod 2012;38:240-4.  Back to cited text no. 19
    
20.
Orstavik D, Eriksen HM, Beyer-Olsen EM. Adhesive properties and leakage of root canal sealers in vitro. Int Endod J 1983;16:59-63.  Back to cited text no. 20
    
21.
Stewart GG. A comparative study of three root canal sealing agents. Oral Surg Oral Med Oral Pathol Oral Radiol Endod 1958;11:1029-41.  Back to cited text no. 21
    
22.
Gurgel-Filho ED, Leite FM, Lima JB, Montenegro JP, Saavedra F, Silva EJ. Comparative evaluation of push-out bond strength of a MTA-based root canal sealer. Braz J Oral Sci 2014;13:114-7.  Back to cited text no. 22
    
23.
Neelakantan P, Subbarao C, Subbarao C, De-Deus G, Zehnder M. The impact of root dentine conditioning on sealing ability and push-out bond strength of an epoxy resin root canal sealer. Int Endod J 2011;44:491-8.  Back to cited text no. 23
    
24.
Gündoğar M. Impact of intracanal calcium hydroxide or triple antibiotic paste on bond strength of root canal sealers: An in vitro study. Cumhuriyet Dent J 2016;19:229-37.  Back to cited text no. 24
    
25.
Sun Y, Li YH, Fan MW. Push-out bond strength of self-adhesive methacrylate resin-based sealers to root dentin. J Huazhong Univ Sci Technolog Med Sci 2014;34:108-13.  Back to cited text no. 25
    
26.
Prather BT, Ehrlich Y, Spolnik K, Platt JA, Yassen GH. Effects of two combinations of triple antibiotic paste used in endodontic regeneration on root microhardness and chemical structure of radicular dentine. J Oral Sci 2014;56:245-51.  Back to cited text no. 26
    
27.
Shakouie S, Shahi S, Samiei M, Milani AS, Reyhani MF, Paksefat S, et al. Effects of different intra canal medicaments on the push out bond strength of endodontic sealers. J Clin Exp Dent 2017;9:e443-7.  Back to cited text no. 27
    
28.
Arslan H, Akcay M, Çakir M, Gok A, Yasa B, Dalli M. Comparison of bond strength of self-etch adhesive to pulp chamber dentin after placement of calcium hydroxide and various antibiotic pastes. Acta Odontol Scand 2015;73:226-31.  Back to cited text no. 28
    
29.
Vilanova W, Carvalho-Junior J, Alfredo E, Sousa-Neto M, Silva-Sousa Y. Effect of intracanal irrigants on the bond strength of epoxy resin-based and methacrylate resin-based sealers to root canal walls. Int Endod J 2012;45:42-8.  Back to cited text no. 29
    
30.
Trindade TF, Barbosa AF, Castro-Raucci LM, Silva-Sousa YT, Colucci V, Raucci-Neto W. Chlorhexidine and proanthocyanidin enhance the long-term bond strength of resin-based endodontic sealer. Braz Oral Res 2018;32:e44.  Back to cited text no. 30
    
31.
Verma D, Taneja S, Kumari M. Efficacy of different irrigation regimes on the push-out bond strength of various resin-based sealers at different root levels: An in vitro study. J Conserv Dent 2018;21:125-9.  Back to cited text no. 31
[PUBMED]  [Full text]  
32.
De-Deus G, Di Giorgi K, Fidel S, Fidel RA, Paciornik S. Push-out bond strength of Resilon/Epiphany and Resilon/Epiphany self-etch to root dentin. J Endod 2009;35:1048-50.  Back to cited text no. 32
    
33.
Ørstavik D, Nordahl I, Tibballs JE. Dimensional change following setting of root canal sealer materials. Dent Mater 2001;17:512-9.  Back to cited text no. 33
    
34.
Souza S, Bombana A, Francci C, Goncalves F, Castellan C, Braga R. Polymerization stress, flow and dentine bond strength of two resin-based root canal sealers. Int Endod J 2009;42:867-73.  Back to cited text no. 34
    

Top
Correspondence Address:
Dr. Alireza Adl
Department of Endodontics, School of Dentistry, Ghasrdast Street, Postal Code: 71956-15878, Shiraz
Iran
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/jcd.jcd_150_22

Rights and Permissions



 
 
    Tables

  [Table 1]



 

Top
 
 
 
  Search
 
 
    Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
    Email Alert *
    Add to My List *
* Registration required (free)  
 


    Abstract
   Introduction
    Materials and Me...
   Results
   Discussion
   Conclusions
    References
    Article Tables

 Article Access Statistics
    Viewed106    
    Printed10    
    Emailed0    
    PDF Downloaded4    
    Comments [Add]    

Recommend this journal