ORIGINAL ARTICLE
Year : 2021  |  Volume : 24  |  Issue : 3  |  Page : 260-264

Effect of blood contamination and various hemostatic procedures on the push-out bond strength of Biodentine when used for furcation perforation repair


1 Department of Conservative Dentistry and Endodontics, Sri Sai College of Dental Sciences, Vikarabad, Telangana, India
2 Department of Public Health Dentistry, Manipal College of Dental Sciences, Manipal Academy of Higher Education, Manipal, Karnataka, India
3 Department of Periodontics, SB Patil Dental College and Hospital, Bidar, Karnataka, India
4 Department of Conservative Dentistry and Endodontics, Manipal College of Dental Sciences, Manipal Academy of Higher Education, Manipal, Karnataka, India

Correspondence Address:
Dr. Manuel S Thomas
Department of Conservative Dentistry and Endodontics, Manipal College of Dental Sciences, Manipal Academy of Higher Education, Manipal- 575 001, Karnataka
India
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/jcd.jcd_229_21

Rights and Permissions

Background: Perforations in the furcation area are common procedural accidents that can impact the outcome of treatment. There are many bioactive materials available to repair these defects. Aim: The purpose of this study was to determine and compare the effect of 25% aluminum chloride solution, 20% ferric sulfate solution, and a 980-nm diode laser, when used for hemostasis, on the dislocation resistance of Biodentine placed to repair furcation perforation. Materials and Methods: This in vitro study was conducted on fifty extracted human permanent mandibular molars, with ten teeth in each group. The stimulated perforations were contaminated with blood, except for one group. The contaminated groups were either treated with aluminum chloride, ferric sulfate, diode laser, or none at all. All the perforations were restored with Biodentine and tested for push-out bond strength. Statistical Analysis Used: One-way analysis of variance and Tukey's HSD post hoc test were applied with a level of significance set at 0.05. Results: The dislocation resistance of Biodentine was found to be highest when aluminum chloride or diode laser was used for arresting bleeding. In contrast, the ferric sulfate group gave the lowest value for push-out bond strength (P < 0.05). Conclusions: According to the present study, the use of ferric sulfate as a hemostatic agent showed a negative effect on the bond strength of the calcium silicate cement to dentin. Furthermore, Biodentine performed better when diode laser and aluminum chloride were used for hemostasis.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed1952    
    Printed84    
    Emailed0    
    PDF Downloaded87    
    Comments [Add]    

Recommend this journal