|Effect of bleaching on color change of composite after immersion in chlorhexidine and coffee
Elham Hasani1, Alireza Akbarzadeh Baghban2, Seyedeh Mahsa Sheikh-Al-Eslamian3, Alireza Sadr4
1 Dental Research Center, Research Institute of Dental Sciences, Dental School, Shahid Beheshti University of Medical Sciences, Tehran, Iran
2 Proteomics Research Center, Department of Biostatistics, School of Allied Medical Sciences, Shahid Beheshti University of Medical Sciences,Tehran, Irna
3 Preventive Dentistry Research Center, Research Institute of Dental Sciences, Dental School, Shahid Beheshti University of Medical Sciences, Tehran, Iran
4 Department of Restorative Dentistry, University of Washington School of Dentistry, Seattle, WA, USA
Click here for correspondence address and email
|Date of Submission||21-Jan-2019|
|Date of Acceptance||04-May-2020|
|Date of Web Publication||20-Aug-2020|
| Abstract|| |
Background: Since the introduction of resin composites, the staining of resin-based materials by colored solutions such as coffee, tea, chlorhexidine (CHX), and other beverages has become a common concern.
Aim: The aim of this study was to evaluate the effect of home and office bleaching as a treatment for discoloration of composite after immersion in coffee or CHX.
Materials and Methods: A microhybrid composite (Z250), nanohybrid composite (Z550), and nanofill composite (ultimate, body shade) were selected. Forty disk shape specimens (8 mm diameter and 2 mm thickness) for each composite were prepared then divided into two groups according to staining solutions (25 g of coffee in 250 ml water, 20 min/day or 0.2% CHX, 1 min/day). Following 1 month staining, specimens were divided into two groups again. Half of the specimens was bleached with in office bleaching agent (Opalescence Boost 40% hydrogen peroxide concentration) 3 times in one visit for 15minutes and the others subjected to home bleaching agent(Opalescence 10% carbamide peroxide) 6h/day until 2 weeks both from Ultradent Products, Inc., South Jordan, UT, USA. Color of the specimens was measured with a spectrophotometer using CIELAB color space at baseline, after 1 month staining, and after ending the bleaching process.
Statistical Analysis: Analysis of variance was used to analyze the data (P < 0.05).
Results: Coffee and CHX provided significant color changes in all groups (P < 0.05). Z550 was the material more prone to discoloration in coffee in comparison with Filtek Ultimate (P = 0.003). After bleaching, materials showed significant reduction except stained Z550 by coffee in home bleaching groups. Both home and office bleaching provided significant color changes in all CHX groups (P < 0.05).
Conclusion: Coffee produced more color changes than CHX. The hydrogen peroxide has the same whitening effect in comparison with carbamide peroxide.
Keywords: Bleaching; carbamide peroxide; chlorhexidine; coffee; color; composite resin; extrinsic stain; hydrogen peroxide
|How to cite this article:|
Hasani E, Baghban AA, Sheikh-Al-Eslamian SM, Sadr A. Effect of bleaching on color change of composite after immersion in chlorhexidine and coffee. J Conserv Dent 2019;22:529-32
|How to cite this URL:|
Hasani E, Baghban AA, Sheikh-Al-Eslamian SM, Sadr A. Effect of bleaching on color change of composite after immersion in chlorhexidine and coffee. J Conserv Dent [serial online] 2019 [cited 2023 Mar 27];22:529-32. Available from: https://www.jcd.org.in/text.asp?2019/22/6/529/292668
| Introduction|| |
Increased esthetic demands by patients, improvements in formulation, and simplification of bonding procedures resulted in increasing clinical use of composite resins over the past few years. Nevertheless, composite resins are recommended for the restoration of all types of class of cavities in all teeth. Since their introduction, the staining of resin-based materials by colored solutions such as coffee, tea, chlorhexidine (CHX), and other beverages has become a common concern. The staining caused by these beverages and solutions varies according to their composition and properties. Both science and technology of dental composite restorative materials have advanced to solve this problem. The resin-based materials that have been on the market have improved their physical properties due to new filling concepts and matrix changes. Unfortunately, discoloration is still a problem for dental resin composite restorations.
Composite surface discoloration by the deposition of extrinsic stains is currently treated by professional cleaning, polishing, bleaching, and in severe cases might be replaced., Up to date, a limited number of studies have reported the color change of tooth-colored materials due to bleaching treatments. The aim of thisin vitro study was to evaluate the effect of home and office bleaching as a treatment for discoloration of composite after immersion in CHX and coffee solution.
| Materials and Methods|| |
Three light-cured methacrylate-based resin composites, microhybrid composite (Filtek Z250), nanohybrid composite (Filtek Z550), and nanofill composite (Filtek Ultimate, body shade), were selected for this study. Detailed information of the materials is presented in [Table 1].
Specimens (8 mm diameter and 2 mm thickness, n = 40 for each composite resin) were prepared using a stainless steel mold. After applying the composite resin, a Mylar strip was placed and pressed with a glass slide to obtain a flat surface. The specimens were cured for 40 s using a halogen light-curing unit (Optilux 501 L.C; Kerr Corporation, Orange, CA, USA). The specimens were removed from the mold and assessed visually for void and structural defects. Defected specimens were excluded from the study. In the next step, the specimen surfaces were finished and polished using grit-600, 800, and 1000 silicon carbide paper, respectively. Then, baseline color was measured using a spectrophotometer ( X-Rite, Grand Rapids, MI, USA).
Specimens were stored at 37°C in distilled water for 24 h. Thereafter, twenty specimens were stored in coffee (25 g in 250 ml of boiling water) 20 min/day, and the other twenty specimens were immersed in 0.2% CHX mouthwash solution 1 min/day until 1 month. All specimens remained in distilled water at 37°C in the incubator between the staining intervals. The color measurements were taken after 1 month staining using a spectrophotometer.
Following coloring intervals, stained specimens of each composite material were divided randomly into two groups. Ten specimens in each group were exposed to office bleaching agent The treatment was performed according to manufacturer's instruction only for one visit; during each visit, the application of the material was repeated three times. The office bleaching agent was Opalescence Boost 40% hydrogen peroxide concentration (Ultradent Products, Inc., South Jordan, UT, USA). Opalescence Boost 40% is a red gel supplied in two separate syringes, which were mixed and applied with a mixing tip for three cycles of 15 min each in one visit.
For the other ten specimens, the home bleaching technique, 10% carbamide peroxide (Opalescence 10%, Ultradent Products, USA) was placed on each sample surface, using a dispenser tip, forming a layer that was up to 1 mm thick. Bleaching agent was left in contact with each tooth sample for a period of 6 h daily until 2 weeks and was subsequently removed using cotton pellet and rinsing. During bleaching intervals, specimens were maintained in the incubator at 37°C. This procedure was repeated on a daily basis for a total of 2 weeks. After bleaching, color measurements were taken again.
The colorimeter displayed the different color parameters (L*, a*, and b*) according to the CIELAB color system, where L* describes the luminance reflectance, whereas a* and b* describe the red-green and yellow-blue color coordinates, respectively.
The change in color from the baseline was calculated after staining (ΔE1) and after the bleaching sessions (ΔE2). The change in color after the staining compared to the color after bleaching (ΔE3) was also calculated. ΔE values were obtained using the Hunter's equation.
ΔE = ([ΔL]2 + [Δa]2 + [Δb]2)1/2
All data were analyzed with the statistical software SPSS Version 23 (SPSS Inc., Chicago, IL, USA). The distributions were assessed and found to be normal (Kolmogorov–Smirnov test). A three-way and two-way analysis of variance (ANOVA) test was applied to determine whether significant differences existed among the groups. Tukey's test was applied as post hoc to evaluate pairwise comparisons. Significance was predetermined at P < 0.05.
| Results|| |
Descriptive statistics (mean and standard deviation [SD]) of stained composite are summarized in [Table 2]. Two-way ANOVA showed that storage medium (P = 0.003) and material (P < 0.001) can affect ΔE1. Coffee and CHX provided significant color changes in all groups (P < 0.05). Coffee resulted in greater discoloration in comparison with CHX. Tukey's HSD (honestly significant difference) test showed that Filtek Z550 exhibited significantly higher values than Filtek Ultimate in coffee (P = 0.003). No significant differences were found when comparing other groups (P > 0.05).
Mean ± SD of ΔE2,3 after composite bleaching is shown in [Table 2]. Three-way ANOVA showed that all factors (material, media, and bleaching agent) have influence on ΔE2(P < 0.001, P < 0.001, and P = 0.004, respectively). After the bleaching procedure, materials tested showed significant reduction except stained Filtek Z550 by coffee in home bleaching groups (ΔE2= 4.50 ± 0.39). Coffee groups had significantly higher ΔE2 values in comparison with CHX groups in all materials (P < 0.001). In CHX stained groups, there are no significant differences in ΔE2 values after home and office bleaching.
Three-way ANOVA showed that none of the factors (material, media, and bleaching agent) have significant influence on ΔE3(P = 0.149, P = 0.202, and P = 0.082, respectively). Both home and office bleaching provided significant color changes in all groups (P < 0.05), which is clinically acceptable (ΔE3< 3.3).
| Discussion|| |
Composite resin discoloration is a result of interactions between external colorants and the physicochemical properties of composite resin materials. The adsorption of external colorants onto the surface and the absorption of such into the resin matrices can both cause color changes and compromise the esthetic outcomes. While restorative materials have been tested in the past, new restorative composite resin materials require further investigation to solve the discoloration behavior as a problem.
The influence of background is quite a controversial topic; in fact, it has been claimed to have no, little or, great influence on color perception., Black and gray backgrounds better simulate the intraoral environment than white background. It was, therefore, decided to perform these measurements against natural gray background.
The color stability of a resin composite material is affected by many chemical factors of its resin components such as purity of the oligomers and monomers, concentration/type of activators, initiators and inhibitors, oxidation of unreacted carbon–carbon double bonds, filler loading, and color of the inorganic pigments.,,, Regarding the proportion of monomers in resin composition, high level of bisphenol A glycidyl methacrylate (bis-GMA, having hydrophilic hydroxide groups) present more water sorption and more susceptibility to staining than those having a high proportion of urethane dimethacrylate (UDMA, resin-containing aliphatic chains that are less hydrophilic). In this regard, all composites demonstrated discoloration for the two staining solutions, especially for the coffee group. Furthermore, coffee seems to be responsible for the more staining because of acidic pH and more affinity to the polymer network.
For enhancing the healing after surgical procedures in the oral environment, the Food and Drug Administration (FDA) suggested a use of CHX (at 0.12% and 0.2% concentrations) recommended as oral rinses of 10–15 ml, for about 30 s, for a limited period of time (respectively, 1 month or 2 weeks). Hence, the discoloration by CHX as a side effect was investigated after 1 month. Several studies have investigated the effect of CHX and noted acceptable color changes (ΔE <3.3) as a side effect but with a slightly redder and darker appearance., Our results showed that all composites have been reached to ΔE >3.3 after immersion in CHX. The discrepancies could be attributed to the types of materials and duration of contact with the solutions and surface texture following different surface treatments.,
Filtek Z550 showed the highest discoloration (ΔE) after immersion in coffee, significantly different from Z250 and Filtek Ultimate (P < 0.001). Greater staining in Filtek Z550 may be due to the wide distribution of particle sizes of this material. Materials with higher particle size, around 15 μm, tend to have lower performance in surface texture compared to materials with a mean particle size inferior to 1 μm, such as Filtek Ultimate.
Since their introduction, the use of bleaching agents has become increasingly popular for whitening stained teeth., Bleaching effect of the bleaching agents on the same material might be different and could be attributed to their different contents. In our study, home bleaching systems were determined to be as effective as office bleaching system except in Z550 group. It may be due to its more color change in coffee and alterations in the surface. The color change of all composite resins bleached with hydrogen peroxide and carbamide peroxide solution was clinically detectable to the naked eye. The results of this study showed that the bleaching agents were produced clinically acceptable discoloration in removing the external staining for dental resin composites. The advantage of bleaching in comparison with polishing procedures for the elimination of stains is ease of availability and better access to the interproximal surface. Thus, patients should be advised that stained composite restorations may be treated by bleaching.
| Conclusion|| |
Coffee and CHX solutions can affect the color of composite resin materials used in this study. Extrinsic color change of nanofill, nanohybrid, and microhybrid composite resins bleached with 10% carbamide peroxide or 40% hydrogen peroxide bleaching agents results in the same outcome.
The authors would like to thank the Dental Research Center, Research Institute of Dental Sciences, Shahid Beheshti University of Medical Science, Tehran, Iran.
Financial support and sponsorship
Conflicts of interest
There are no conflicts of interest.
| References|| |
Ritter AV. Sturdevant's Art and Science of Operative Dentistry-e-Book. New York NY, United States: Elsevier Health Sciences; 2017.
Shamszadeh S, Sheikh-Al-Eslamian SM, Hasani E, Abrandabadi AN, Panahandeh N. Color stability of the bulk-fill composite resins with different thickness in response to coffee/water immersion. Int J Dent 2016;2016:7186140.
Lu H, Roeder LB, Lei L, Powers JM. Effect of surface roughness on stain resistance of dental resin composites. J Esthet Restor Dent 2005;17:102-8.
Villalta P, Lu H, Okte Z, Garcia-Godoy F, Powers JM. Effects of staining and bleaching on color change of dental composite resins. J Prosthet Dent 2006;95:137-42.
Türkün LS, Türkün M. Effect of bleaching and repolishing procedures on coffee and tea stain removal from three anterior composite veneering materials. J Esthet Restor Dent 2004;16:290-301.
Ren YF, Feng L, Serban D, Malmstrom HS. Effects of common beverage colorants on color stability of dental composite resins: The utility of a thermocycling stain challenge model in vitro
. J Dent 2012;40 Suppl 1:e48-56.
Ardu S, Braut V, Di Bella E, Lefever D. Influence of background on natural tooth colour coordinates: Anin vivo
evaluation. Odontology 2014;102:267-71.
Lee YK, Powers JM. Influence of background color on the color changes of resin composites after accelerated aging. Am J Dent 2007;20:27-30.
Asmussen E. Factors affecting the color stability of restorative resins. Acta Odontol Scand 1983;41:11-8.
Eldiwany M, Friedl KH, Powers JM. Color stability of light-cured and post-cured composites. Am J Dent 1995;8:179-81.
Eliades T, Gioka C, Heim M, Eliades G, Makou M. Color stability of orthodontic adhesive resins. Angle Orthod 2004;74:391-3.
Abu-Bakr N, Han L, Okamoto A, Iwaku M. Color stability of compomer after immersion in various media. J Esthet Dent 2000;12:258-63.
Ardu S, Braut V, Gutemberg D, Krejci I, Dietschi D, Feilzer AJ. A long-term laboratory test on staining susceptibility of esthetic composite resin materials. Quintessence Int 2010;41:695-702.
Bagheri R, Burrow MF, Tyas M. Influence of food-simulating solutions and surface finish on susceptibility to staining of aesthetic restorative materials. J Dent 2005;33:389-98.
Marrelli M, Amantea M, Tatullo M. A comparative, randomized, controlled study on clinical efficacy and dental staining reduction of a mouthwash containing chlorhexidine 0.20% and anti discoloration system (ADS). Ann Stomatol (Roma) 2015;6:35-42.
Mutlu-Sagesen L, Ergün G, Ozkan Y, Semiz M. Color stability of a dental composite after immersion in various media. Dent Mater J 2005;24:382-90.
Falkensammer F, Arnetzl GV, Wildburger A, Freudenthaler J. Color stability of different composite resin materials. J Prosthet Dent 2013;109:378-83.
Da Silva JD, Park SE, Weber HP, Ishikawa-Nagai S. Clinical performance of a newly developed spectrophotometric system on tooth color reproduction. J Prosthet Dent 2008;99:361-8.
Motro PF, Kursoglu P, Kazazoglu E. Effects of different surface treatments on stainability of ceramics. J Prosthet Dent 2012;108:231-7.
Loguercio AD, Reis A, Rodrigues Filho LE, Busato AL. One-year clinical evaluation of posterior packable resin composite restorations. Oper Dent 2001;26:427-34.
Türkün LS, Aktener BO. Twenty-four-month clinical evaluation of different posterior composite resin materials. J Am Dent Assoc 2001;132:196-203.
Dr. Seyedeh Mahsa Sheikh-Al-Eslamian
Dental Research Center, Research Institute of Dental Sciences, Shahid Beheshti University of Medical Sciences, Evin, Tehran
Source of Support: None, Conflict of Interest: None
[Table 1], [Table 2]
|This article has been cited by|
||Effect of single serve sachet powder drinks on color stability of a nano hybrid composite resin
| ||Ebru AKLEYIN, Elif Pinar BAKIR, Samican ÜNAL, Gamze POLAT, Merve YENIÇERI ÖZATA |
| ||Journal of Health Sciences and Medicine. 2023; 6(1): 13 |
|[Pubmed] | [DOI]|
||In Vitro Color Stability Evaluation of Three Polished and Unpolished Nanohybrid Resin Composites Immersed in a 0.12% Chlorhexidine-Based Mouthwash at Different Times
| ||Reyna Allccahuaman-Avalos, Ramín Medina-Sánchez, Leonor Castro-Ramirez, Marysela Ladera-Castañeda, Luis Cervantes-Ganoza, Reynaldo Martínez-Campos, Fredy Solís-Dante, Ana Aliaga-Mariñas, Arturo Verástegui-Sandoval, César Cayo-Rojas |
| ||Polymers. 2023; 15(6): 1339 |
|[Pubmed] | [DOI]|
||KARANFIL VE YESIL ÇAYIN RESTORATIF MATERYALLERIN YÜZEY VE OPTIK ÖZELLIKLERI ÜZERINE ETKISI: IN VITRO ÇALISMA
| ||Zeynep BUKET KAYNAR, Tolgahan DOGAN, Nazmiye DÖNMEZ, Magrur KAZAK |
| ||Atatürk Üniversitesi Dis Hekimligi Fakültesi Dergisi. 2022; : 1 |
|[Pubmed] | [DOI]|
||Direct Radiotherapy-Induced Effects on Dental Hard Tissue in Combination With Bleaching Procedure
| ||Eva Klaric Sever, Andro Tarle, Majana Soce, Timor Grego |
| ||Frontiers in Dental Medicine. 2021; 2 |
|[Pubmed] | [DOI]|
| Article Access Statistics|
| Viewed||4047 |
| Printed||109 |
| Emailed||0 |
| PDF Downloaded||254 |
| Comments ||[Add] |
| Cited by others ||4 |